H13 1.2344 SKD61 Mold Steel Plate For Die Casting Mold Base
Descriptiion
H13 steel is the most representative hot-working tool steel which
was used widely. Such as molds for extrusion and metal die-casting
molds. It also is called DIN 1.2344 and JIS SKD61 steel. H13 steel
round bar sheet plate heat treatment requirements are very strict.
The great annealing processing would improve the performance of
steel. H13 steel chemical composition and more information as
below.
| Stand | C (%) | Si (%) | Mn(%) | P (%) | S (%) | Cr (%) | Mo (%) | Ni (%) |
|---|
| ASTM A29/A29M-05 | 0.18-0.23 | 0.15-0.35 | 0.70-0.90 | ≤0.035 | ≤0.040 | 0.40-0.60 | 0.15-0.25 | 0.40-0.70 |
| EN 10084-2008 | 0.17-0.23 | 0.40 | 0.65-0.95 | ≤0.025 | ≤0.035 | 0.35-0.70 | 0.15-0.25 | 0.40-0.70 |
| JIS G4053-2008 | 0.17-0.23 | 0.15-0.35 | 0.60-0.90 | Max0.030 | Max0.030 | 0.40-0.60 | 0.15-0.25 | 0.40-0.70 |
| ISO 683/11:1987 | 0.17-0.23 | 0.15-0.40 | 0.65-0.95 | ≤0.035 | ≤0.035 | 0.30-0.65 | 0.15-0.25 | 0.40-0.70 |
H13 Steel Plate Sheet Round Bar Heat Treatment
Annealing
Heat slowly to 1550°-1650°F, hold until entire mass is heated
through, and cool slowly in the furnace (40F per hour) to about
1000°F, after which cooling rate may be increased. Suitable
precautions must be taken to prevent excessive carburization or
decarburization.
Stress Relieving
When desirable to relieve the strains of machining, heat slowly to
1050°-1250°F, allow to equalize, and then cool in still air (Strain
Relieving).
Preheat Prior to Hardening
Warm slightly before charging into the preheat furnace, which
should be operating at 1400°-1500°F.
Hardening
H13 tool steel is a steel having very high hardenability and should
be hardened by cooling in still air. The use of a salt bath or
controlled atmosphere furnace is desirable to minimize
decarburization, and if not available, pack hardening in spent
pitch coke is suggested. The temperature employed is usually
1800°-1850°F, depending on size section.
Quenching
Quench in still air or dry air blast. If complicated forms are to
be hardened, an interrupted oil quench can be used. Quench part in
oil and remove from the bath when it just loses its color
(1000°-1100°F). Finish cooling to below 150°-125°F in air, then
tempers immediately.
Tempering
Tempering is carried out in 1.2344 tool steels from 538 to 649°C
(1000 to 1200°F) to obtain Rockwell C hardness of 53 to 38. Double
tempering can also be performed in these steels for every one hour
at the preferred tempering temperature.
Why Choose Us
Why Choose Us
1) Best service with 24 hours reply.
2) Approved by ISO9001,CE,SGS every year.
3) Competitive price andquality from our own factory.
4) Flexible payment with T/T,L/C,Trade Assurance.
5) Smooth production ability(1000tons/month).
6) Quick delivery and standard exporting package.
Product Display
Factory Manufacture Process:
Delivery
FAQ
1. who are we?
We are based in Henan, China, start from 2001,sell to
Africa(30.00%),Eastern Asia(25.00%),South Asia(20.00%),Mid
East(15.00%),South America(10.00%). There are total about 11-50
people in our office.
2. how can we guarantee the quality?
Always a pre-production sample before mass production;
Always final Inspection before shipment;
3. what can you buy from us?
CRC,CRFH,GI,PPGI,SECTIONS